Science, Tech, Math › Science Titanium Properties and Characteristics This metal has aerospace, military and medical applications Share Flipboard Email Print Monty Rakusen/Cultura/Getty Images Science Chemistry Chemistry In Everyday Life Basics Chemical Laws Molecules Periodic Table Projects & Experiments Scientific Method Biochemistry Physical Chemistry Medical Chemistry Famous Chemists Activities for Kids Abbreviations & Acronyms Biology Physics Geology Astronomy Weather & Climate By Terence Bell University of British Columbia Carleton University Terence Bell wrote about commodities investing for The Balance, and has over 10 years experience in the rare earth and minor metal industries. our editorial process Twitter Twitter LinkedIn LinkedIn Terence Bell Updated October 31, 2019 Titanium is a strong and lightweight refractory metal. Titanium alloys are critical to the aerospace industry, while also being used in medical, chemical and military hardware, and sporting equipment. Aerospace applications account for 80% of titanium consumption, while 20% of the metal is used in armor, medical hardware, and consumer goods. Properties of Titanium Atomic Symbol: TiAtomic Number: 22Element Category: Transition MetalDensity: 4.506/cm3Melting Point: 3038°F (1670°C)Boiling Point: 5949°F (3287°C)Moh's Hardness: 6 Characteristics Alloys containing titanium are known for their high strength, low weight, and exceptional corrosion resistance. Despite being as strong as steel, titanium is about 40% lighter in weight. This, along with its resistance to cavitation (rapid pressure changes, that cause shock waves, which can weaken or damage metal over time) and erosion, makes it an essential structural metal for aerospace engineers. Titanium is also formidable in its resistance to corrosion by both water and chemical media. This resistance is the result of a thin layer of titanium dioxide (TiO2) that forms on its surface that is extremely difficult for these materials to penetrate. Titanium has a low modulus of elasticity. This means that titanium is very flexible, and can return to its original shape after bending. Memory alloys (alloys which can be deformed when cold, but will return to their original shape when heated) are important for many modern applications. Titanium is non-magnetic and biocompatible (non-toxic, non-allergenic), which has led to its increasing use in the medical field. History The use of titanium metal, in any form, only really developed after World War II. In fact, titanium was not isolated as a metal until the American chemist Matthew Hunter produced it by reducing titanium tetrachloride (TiCl4) with sodium in 1910; a method now known as the Hunter process. Commercial production, however, did not come until after William Justin Kroll showed that titanium could also be reduced from chloride using magnesium in the 1930s. The Kroll process remains the most used commercial production method to this day. After a cost-effective production method was developed, titanium's first major use was in military aircraft. Both Soviet and American military aircraft and submarines designed in the 1950s and 1960s began making use of titanium alloys. By the early 1960s, titanium alloys started to be used by commercial aircraft manufacturers as well. The medical field, particularly dental implants and prosthetics, awoke to titanium's usefulness after Swedish doctor Per-Ingvar Branemark's studies dating back to the 1950s showed that titanium triggers no negative immune response in humans, allowing the metal to integrate into our bodies in a process he termed osseointegration. Production Although titanium is the fourth most common metal element in the earth's crust (behind aluminum, iron, and magnesium), the production of titanium metal is extremely sensitive to contamination, particularly by oxygen, which accounts for its relatively recent development and high cost. The main ores used in the primary production of titanium are ilmenite and rutile, which respectively account for about 90% and 10% of production. Close to 10 million tons of titanium mineral concentrate was produced in 2015, although only a small fraction (about 5%) of titanium concentrate produced each year ultimately ends up in titanium metal. Instead, most are used in the production of titanium dioxide (TiO2), a whitening pigment used in paints, foods, medicines, and cosmetics. In the first step of the Kroll process, titanium ore is crushed and heated with coking coal in a chlorine atmosphere to produce titanium tetrachloride (TiCl4). The chloride is then captured and sent through a condenser, which produces a titanium chloride liquid that is more 99% pure. The titanium tetrachloride is then sent directly into vessels containing molten magnesium. In order to avoid oxygen contamination, this is made inert through the addition of argon gas. During the consequent distillation process, which can take a number of days, the vessel is heated to 1832°F (1000°C). The magnesium reacts with the titanium chloride, stripping the chloride and producing elemental titanium and magnesium chloride. The fibrous titanium that is produced as a result is referred to as titanium sponge. To produce titanium alloys and high purity titanium ingots, titanium sponge can be melted with various alloying elements using an electron beam, plasma arc or vacuum-arc melting.